Formation mechanism of intermetallic components during dissimilar diffusion bonding of IN718/BNi-2/AISI 316 L by TLP process

In this research, microstructure and intermetallic components of IN 718/BNi-2/316 L joint were studied. Dissimilar bonding was carried out at a temperature of 1050° C and, bonding time varied at 30 and 45 min in a vacuum furnace under an approximate pressure of 10−5 mbar. After TLP joining, samples...