Solidification morphology and semisolid deformation in the superalloy Rene 108 : Part III Equiaxed solidified microstructures

A high-temperature nickel-base superalloy (Rene 108) was solidified at various cooling rates. The morphology of the equiaxed microstructure and the mechanism for intrinsic microporosity formation were correlated to the processing parameters. A special Gleeble testing procedure (developed previously...

Full description

Bibliographic Details
Published in:Journal of Materials Science, Vol. 29, No. 14 (1994), p. 3637-3642
Main Author: Lin, S.